Two component effect finish topcoat on acrylic resin basis, chemical cured with poly-isocyanate (polyurethane).
Two component effect finish topcoat on acrylic resin basis, chemical cured with poly-isocyanate (polyurethane).
2K-Derocryl Hammerschlag Lack
Two component effect finish topcoat on acrylic resin basis, chemical cured with poly-isocyanate (polyurethane).
Field of application
Properties
| Colours | silver-grey, green, blew |
| Flash point | >23 °C |
| Temperature stability | Up to 120 °C |
| Gloss | Glossy |
| Mixing ratio | Hardener HL 109 |
| (Basis:hardener) by weight | 2,5:1 |
| (Basis:hardener) by volume | 2,5:1 |
| Pot life in hours | 8 |
| Viscosity | Appr. 90 sec running time (DIN 4 mm pot) |
| Density in kg/l | 0,96 |
| Solid content in % | 45 |
| Solid volume in % | 42 |
| Theoretical spreading capacity |
|
| Recommended film thickness | 75 µm WFT corresponds to 30 µm DFT |
| Drying (DIN EN ISO 1517) | 40 µm DFT |
| Dust-dry (Tg1) | After 30 min |
| Touch-dry (Tg4) | After 1 h |
| Dry (Tg6) | After 24 h |
| Cured chemically | After 7 days |